FIBERGLASS APPLICATION ON GELCOAT

By any method applied on the mold hardness reached after sufficient gelcoat of fiber is applied.
* Obtain the first floor we'll be as intricate product patterns very easy to work (which can be wet) thin surface tissue (KORTEL) is applied.
* Mold size according to the cut surface tissue or some sizeable 300gr/m2 'lik thin fibrous glass fiber by weight of polyester that are appropriate to the product amounts to 2 is taken.
* Polyester accelerator to 1% (1% Co) whether the added 1% after being mixed are mixed whether the MEK-peroxide added.
These rates and different applications in different polyester içinş cobalt 0.3% - 3% for Mek Peroxide 0.5% - 2% within the borders can be added.
* Cobalt may shorten the time of the gel to be much further. However, the obvious effect of time on the hardness is not the end.
* The more the Mek Peroxide gel further shorten the time some form, the final hardness (curing time) much reduced.
* Soft polyester came ready to become a very fine brush to the surface of the mold as jelkotlu is driven.
* Then the mold is inserted into the reinforcing material.
* Increased or polyester brush roll with a seal of glass fiber is used wet.
The point here should be considered with the wet glass fiber polyester certain area is not much clutter. Brush is used, and vertically in the form of light pulses with a fiber suppression should be trying to get wet. Rolls should not be used to suppress otherwise than is being used by polyester fiber soaked in binding have been solved can scroll easily.
Other points to note on the first floor is that no air should be left. Observed bubbles should be discarded out with a brush or metal rolls.
Metal rolls can be used here in different diameters. Thin edges and corners should be preferred to those types. This ring has the appearance of rolls arranged side by side, and the gaps between the air bubbles make it easier for the thrown. Same purpose can be used in hedgehog rolls.
* After the first layer of glass fiber reinforced 2 and 3 can continue to ply. However, in intricate patterns to work on the first floor yet again uncured form may result in air bubbles. For this reason, much of the first floor of recessed mold after hardening is more convenient to switch to other floors. After the first coat to be applied the same rules apply for glass fiber reinforced. To use glass fiber thickness (weight per unit area) is increased gradually. The high mechanical strength should be, a coat of GRP products, glass fiber felt is preferred to use a coat of woven glass fiber. However, if a woven polyester / glass woven rate of 1 / 1 should be. GRP work very thick 3 to 4 times the level of fiber hardening after application can be expected later 3 to 4 times should be applied. Otherwise, at the same time 7 8 ply polyester processing in a block will be created to light during an erection products in the heat may cause cracks or internal stress.
* Once full erection sufficient thickness of particles are cut off from overflowing outside the mold and CTP products are expected to be mature.
* However, the end of CTP products to reach the hardness at room temperature for 20 to 25 days will have to wait. This oven is used to shorten the length of time.